ASME SA709 Grade 50 weather resistant steel plate
Origin: bbn STEELThickness: 6mm to 350mm
Length: 200mm to 18000mm
Payment terms: L/C, T/T
Commitment: If we have no the size in stock, it takes about 20 days for us to produce the ASME SA709 Grade 50 weather resistant steel plate for you if the quantity can be more than 10 tons.
Describe:Hot rolled steel strip with JIS standard SPHC - shenda-steel…Hot rolled steel strip with JIS standard SPHC,US $ 310 - 490 / Metric Ton, AISI, ASTM, BS, DIN, GB
Inquiry (Leave message and get the latest price)ASME SA709 Grade 50 weather resistant steel plate Equivalent
ASME SA709 Grade 50 weather resistant steel plate
ASME SA709 Grade 50 weather resistant steel plate is a kind of low alloy structural steel used in the construction of ordinary structural Bridges.. In order to obtain better weather resistance, ASME SA709 Grade 50 weather resistant steel plate is generally used for external use.
ASME SA709/SA709M Grade 36 Steel Coil
C max | Si max | Mn | P max | S max | Cu min |
0.25 | 0.40 | - | 0.04 | 0.05 | 0.20 |
Yield Strength (MPa) min. | Tensile Strength (MPa) min. | Elongation in 8 in. min. % | Elongation in 2 in. min. % | ||
250 | 400 | 20 | 23 |
C max | Si max | Mn max | P max | S max | Cu |
0.23 | 0.40 | 1.35 | 0.04 | 0.05 | 1 |
Yield Strength (MPa) min. | Tensile Strength (MPa) min. | Elongation in 8 in. min. % | Elongation in 2 in. min. % | ||
345 | 450 | 18 | 21 |
C max | Si max | Mn | P max | S max | V max | Nb | Cu max | Ni max | Cr max | Mo max | - |
0.23 | 0.40 | 0.50-1.60 | 0.04-35 | 0.045 | 0.15 | 0.05 | 0.60 | 0.45 | 0.35 | 0.15 | - |
Yield Strength (MPa) min. | Tensile Strength (MPa) min. | Elongation in 8 in. min. % | Elongation in 2 in. min. % | ||||||||
345 | 450 | 18 | 21 |
C max | Si max | Mn | P max | S max | V max | Nb | Cu max | Ni max | Cr max | Mo max | Ai min |
- | - | - | 0.035 | 0.035 | - | - | - | - | - | - | 0.020 |
Yield Strength (MPa) min. | Tensile Strength (MPa) min. | Elongation in 8 in. min. % | Elongation in 2 in. min. % | ||||||||
345 | 485 | 18 | 21 |
C max | Si | Mn | P max | S max | V max | Nb | Cu | Ni | Cr | Mo | Ai |
0.11 | 0.30-0.50 | 1.10-1.35 | 0.020 | 0.006 | 0.04-0.08 | - | 0.25-0.40 | 0.25-0.40 | 0.45-0.70 | 0.02-0.08 | 0.010-0.040 |
Yield Strength (MPa) min. | Tensile Strength (MPa) min. | Elongation in 8 in. min. % | Elongation in 2 in. min. % | ||||||||
345 | 485 | 18 | 21 |
C max | Si | Mn | P max | S max | V max | Nb | Cu | Ni | Cr | Mo | Ai |
0.11 | 0.30-0.50 | 1.10-1.35 | 0.020 | 0.006 | 0.04-0.08 | - | 0.25-0.40 | 0.25-0.40 | 0.45-0.70 | 0.02-0.08 | 0.010-0.040 |
Yield Strength (MPa) min. | Tensile Strength (MPa) min. | Elongation in 8 in. min. % | Elongation in 2 in. min. % | ||||||||
485 | 585-760 | - | 19 |
C | Mn | Si | P | S |
0.26 | 0.4-0.9 | 0.4 | 0.04 | 0.05 |
Tensile Strength(MPa) | Yield Strength(MPa) | % Elongation in 2 in.(50mm) min | Impacting Test Temperature | |
400-650 | 250 | 20 | +20,0,-20 |
C | Mn | P | S | Si | Cu | |
≤0.08 | 0.95-1.50 | ≤0.015 | ≤0.006 | 0.15-0.50 | 0.90-1.20 | |
Ni | Cr | Mo | V | Al | N | Nb |
0.65-0.90 | 0.4-0.65 | 0.4-0.65 | 0.04-0.08 | 0.02-0.05 | ≤0.015 | 0.01-0.03 |
Thickness | Yield Strength | Tensile Strength | Elongation | Charpy V Impact Test | ||
Degree | Energy 1 | Energy 2 | ||||
mm | Min Mpa | Mpa | Min % | - | J | J |
5<t≤300 | 690 | 760-895 | 18 |
C max | Si | Mn | P max | S max | V max | Nb | Cu | Ni | Cr | Mo | Ai |
0.08 | 0.15-0.35 | 0.95-1.50 | 0.015 | 0.006 | 0.04-0.08 | 0.01-0.03 | 0.90-1.20 | 0.65-0.90 | 0.40-0.65 | 0.40-0.65 | 0.020-0.050 |
Yield Strength (MPa) min. | Tensile Strength (MPa) min. | Elongation in 8 in. min. % | Elongation in 2 in. min. % | ||||||||
485 | 585-760 | - | 19 |